IOTA R31000 silazane ceramic precursor adhesive

    IOTA R31000 silazane ceramic precursor adhesive  


    Product characteristics: Room temperature curing, short curing time, excellent temperature resistance, temperature resistance 800-1000℃

    Product description: Three-components silazane ceramic precursor adhesive.

    Product application: The product can be used for bonding and sealing between metals, ceramics or composite materials and preparing high temperature resistant coating materials.

    Packing: 0.5L~10L plastic drum or customized according to customer requirements

    Technical index:

    Appearance: gray black, no solvent

    Viscosity: ~5000cp

    Performance index:

    Tensile strength at room temperature>4MPa, tensile strength at 400℃>3MPa

    Tensile shear strength at 600℃>3MPa,Tensile shear strength at 800>2MPa

    Tensile shear strength at 1000℃ >1MPa

    Aging at 400℃ for 7 days, room temperature bond strength 6.11MPa

    Aging at 450℃ for 7 days, room temperature bond strength 7.28MPa

    Aging at 600℃ for 5h, bonding strength at 600 8.15 MPa

    Aging at 600℃ for 300h, room temperature bond strength 10.17MPa, 600 bond strength 10.5MPa,

    Aging at 600°C for 5 hours, cooling to room temperature, 10 cycles of high and low temperature, 600°C bond strength 6.16MPa

    Curing conditions: operating time 30 minutes, curing process: room temperature, 5~7 days

    Storage: The shelf life of curing agent is 1 year; After the curing agent is unsealed, its validity is affected by the protection measures, the validity  is about 6 months at dry and cool place condition. It is should be stored in a cool and dry place.


    Note: Ammonia gas will overflow when the cap is opened after long time. It is best to use it in a ventilated environment.